Basalt Volcanic Composites

What are Basalt Fibers?

They are Pultruded fibers made from volcanic rock melted in
high heat furnaces. Pultrusion is a manufacturing process for
producing continuous lengths of FRP (fiber reinforced polymer)
structural shapes. Raw materials include a liquid resin mixture
(containing resin, fillers and specialized additives) and reinforcing fibers. The process involves pulling these raw materials
(rather than pushing as is the case in extrusion) through a
heated forming die using a continuous pulling device.

Basalt FRP is a Composite Rebar (BCR)

Basalt rebar is made as a continuous spiral formed by winding
fibers into a highly durable compound. These fibers form a
strong composite offering a wide range of applications for
construction. Basalt rebars are resistant to corrosion and
aggressive chemical liquids and are extremely light (4 times
lighter than steel), producing considerably longer life
expectancy in construction.

The Main Uses of Basalt Products are

Textile applications for fire protection :
Basalt does not melt nor shrink in flame and when not mechanically stressed, keeps its geometric integrity.
Basalt is exceptionally suited to block fire. Basalt products
resist open flame. A fabric made of Basalt, with a Bunsen
burner pointed at it (1100 - 1200C) becomes red hot as a metal
fabric would. This can last for hours. For reference, an E-glass
fabric of the same surface density gets pierced by the same
flame in a matter of seconds.
High Temperature Insulation (HTI) :
Basalt fibers, at present, exhibit a resistance to temperature
superior to E glass fibers in the range -260 to +560C. A
perfect high temperature insulation material chopped Basalt
fibers and non-woven Basalt needled mats find their place in
the construction of auto and motorcycle exhaust mufflers and
ovens. They are also used as the heat insulation of gas turbines,
including nuclear plant locations, as basalt is known to resist
degradation caused by radiation, unlike synthesized materials
such as glasses. Basalt is also functional to very low temperatures (down to 260C). Other useful applications are insulation
of liquid nitrogen tanks and pipes, and cryogenics.
continued on page 2 >>

Top Ten Reasons

to use Basalt Fibers
1.

Stronger than fiberglass in tensile strength

2. Non-respirable, inert and safe to work with

3. 18% better elastic modulus
4. UV immune
5. Non-conductive
6. Will not harbor bacterial or microbial
growth
7.

Better impact resistance, does not shatter

like carbon fibers

8. Ten times better electrical insulator than

fiberglass
9. Very resistant to aggressive liquids, acids
and alkalies
10. Has great sound attenuation properties
Oh yes! There are more reasons...cont. pg 4 >>

The Main Uses of Basalt Products continued

As reinforcement in composite materials :
The great mechanical properties of Basalt (strength &
rigidity), easy wetting of the filament surface and
recyclability make them particularly suitable for composites applications.
UV resistance, better acid resistance, better alkaline
resistance and very low water absorption of Basalt
fibers ensure excellent weatherability for outdoor Basalt
fiber reinforced composites.
Higher thermal insulation and equally high electrical
resistivity of Basalt fibers also allow making reinforced
composites with good dielectric properties and better
heat diffusion. Basalt is ten times better electrical
insulator than fiberglass.
Basalt fiber reinforced injection molded parts have a
better surface finish. This allows direct utility as an
automotive interior decorative component.
Basalt continuous fibers have a melting temperature
higher than that of the flame, which allows separation of
the composite constitutions by fire at the recycling
stage (e.g. in automotive industry). There is no disposal
issue at the recycling stage after separation, being a
natural product.

For more Basalt Product Uses

go to www.basalt.guru

NEW! Bio-Mid & Basalt Fabric

Smarter Building Systems is proud to announce the
next generation of fibers made from renewable
materials using Basalt fibers and a cellulose fiber
Bio-Mid, made from certified sustainable wood.
Bio-Mid and Basalt volcanic rock fibers are
compatible with most common resin systems.
These fibers have unique advantages to traditional
natural fibers they offer the same lightweight and
sustainable advantages, but with a substantial increase
in thermal resistance, fiber uniformity, and fiber
alignment. Results are a much higher in-plane loading
and higher fiber content in laminates.
Breaking strengths are higher than most E-glass yarns
of similar weight. 100% renewable content.
Cellulose is the worlds most abundant renewable
material, and basalt mines contain many millions of
cubic yards of volcanic rock.

No fertilizers, pesticides or extraordinary irrigation are

required to produce these fibers. They do not compete
or displace lands suitable for food crops. All this makes
for a much lower carbon footprint in stark contrast to
traditional natural or man-made synthetic or petroleum
based fibers that often generate thousands of tons of
CO2 due to post harvesting and mining processes.
Manufacturing with a conscience, with technology that
can create superior performance, while remaining
earth-friendly.
Fabrics are available in standard 40-inch (1 meter)
widths and can be supplied in other widths ranging from
30-80 inches (76 cm up to 2 meters). Combined as a
unique hybrid, the Bio-Mid/Basalt fibers are particularly
useful as the different properties are advantageous.
Phone (401) 481 8422 or email Nick
today for more Information.

Ph: 401.481.8422 | Email: [email protected] | www.smarter-building-systems.com | www.basalt.guru

Selection of Basalt Products

BASALT PRODUCTS: Weaves, Weights, Dimensions, etc.

UNI-DIRECTIONAL FABRIC
Plain: 200 grams/m2; 300 grams/m2; 13 micron roving
Black: 200 grams/m2; Black 13 micron roving

25mm Mesh

5mm Mesh

Fabric

MULTI-DIRECTIONAL FABRIC
Bi-Axial: 450 grams/m2; fiber angles +45, - 45; 13 micron roving.
Bi-Axial: 450 grams/m2; fiber angles 0, 90; 13 micron roving.
Bi-Axial: 650 grams/m2; fiber angles 0, 90; 13 micron roving.
Tri-Axial: 980 grams/m2; fiber angles 0, +45, - 45; 13 micron roving.
Quad-Axial: 680 grams/m2; fiber angles 0, 90, +45, -45; 13 micron roving.
PLAIN WEAVE FABRIC
15x15: 108 grams/m2; 9 micron fibers. 65 grams/m2; 13 micron fibers.
180 grams/m2; 13 micron fibers. 200 grams/m2; 9 micron fibers.
7.2x7.2 : 220 grams/m2; 19 micron fibers.
5x5: 325 grams/m2. 11 micron fibers.
5x3.5: 400 grams/m2; 11 micron fibers.
5x3: 650 grams/m2; 13 micron fibers.

Tape

TWILL WEAVE FABRIC

8x7: 200 grams/m2. 9 micron fibers.
5x5: 350 grams/m2. 13 micron fibers.
6x6: 900 grams/m2. 13 micron fibers.

36mm Chopped Fiber

SATIN WEAVE FABRIC: 220 grams/m2. 300 grams/m2. 9 micron fibers.

COATED FABRIC: Aluminum Coated one side 200 grams/m2.
220 grams/m2. 650 grams/m2.
3mm Chopped Fiber

SURFACE VEIL (WET-LAID NON-WOVENS): 30 grams/m2. 40 grams/m2.

WOVEN TAPE: 25mm. 50mm. 75mm. 100mm. 135mm.
Heavy weight 25mm x 2mm thick.
TWILL WOVEN TAPE: 50mm. Plain or Aluminum coated one side
BI-AXIAL BRAIDED SLEEVING: Diameter 5 cm. 7 cm. 10 cm. 15 cm.
6mm, 8mm, 12mm,
25mm Rebar

CHOPPED STRAND MAT: 200 grams/m2. 350 grams/m2.

CHOPPED FIBER: Length 3mm. 6mm. 9mm. 12mm. 18mm. 24mm.
30mm. 36mm. 50mm. 63mm. 90mm.
CONTINUOUS ROVING: 9 micron/136 tex. 13 micron/800 tex.
13 micron/1200 tex. 16 micron/2400 tex. 16 micron/4800 tex.
3-PLY ROPE: 3 plies of 6400 tex 16 micron roving, total tex 19,200

Needle Felt Mat

GUN ROVING: 15 micron/2400 tex

REBAR: Diameter 4mm. 6mm. 8mm. 10mm. 12mm. 25mm.
MESH: Plain or Resin Coated. Window size 5mm x 5mm. 10mm x 10mm.
25mm x 25mm. 50mm x 50mm.
NEEDLE FELT MAT: Thickness 6mm. 8mm. 12mm. 25mm.

Surface Veil

RIGID BOARD: Thickness 6mm. 12mm. 18mm.

More Reasons
to use Basalt Fibers!
Much higher heat and extreme cold
cryogenics are made with basalt and
so are fire curtains

Comparative Technical Characteristics of Filament

Made from E-Glass, Basalt and Silica
SI Units

Basalt
Filaments

Thermal
Maximum application temperature
Sustained operating temperature
Minimum operating temperature
Thermal conductivity
Melting temperature
Vitrification conductivity
Glow loss
Thermal expansion coefficient

(C)
(C)
(C)
(W/m K)
(C)
(C)
(%)
(ppm/ C)

650
600
-260
0.031-0.038
1450
1050
1.91
8.0

600
480
-60
0.034-0.04
1120
600
0.32
5.4

1100
1000
-170
0.035-0.04
1550
1300-1670
1.75
0.05

Basalt sleeves with no seams come

in many sizes used as spark plug
covers for example

Physical/Mechanical
Density
Filament diameter
Tensile strength
Compression
Elastic modulus
Linear expansion coefficient
Elongation at break
Absorption of humidity (65%RAH)
Stability at tension (20 C)
Stability at tension (200 C)
Stability at tension (400 C)

(g/cm3)
(microns)
(M Pa)
(psi)
(G Pa)
(x10 /K)
(%)
(%)
(%)
(%)
(%)

2.75
9-23
4840
550,000
89
5.5
3.15
<0.1
100
95
82

2.6
9-13
3450
440,000
77
5
4.7
<0.1
100
92
52

2.15
9-15
4750
510,000
66
0.5
1.2
<0.1
100
94
80

Basalt boards with a fire retardant

resin are a perfect backer with fire
and insulation properties

Acoustics
Sound absorption coefficient

(%)

0.9-0.99

0.8-0.93

0.85-0.95

(ohm.m)
(1 MHz)
(1 MHz)

1*1012
0.005
2.2

1*1011
0.0047
2.3

1*1011
0.0049
2.3

0.2
5.0
2.2

0.7
6.0
38.9

0.05
5.0
15.7

$$$$

Much better pricing than S-glass,

Kevlar and carbon fiber
A beautiful golden color
Supple many weights and weaves
available. Plain, satin, coated.
Many times lighter than steel and yet
2-3 times stronger than steel

Properties

Fiberglass

Silica
Filament

Will not corrode

Does not interfere with RF signals
Ballistic impact properties
Made from rock the concrete basalt
products expand and contract at the
same rate unlike others
Great for making tool molds as
basalt takes heat and does not
conduct and does not move

Basalt twine rope acts like a flexible

rebar a ten pound box of over a
thousand feet!

Industries Currently
Testing Basalt
Cryogenics
Prosthetics
Filament Winding
Thermoplastics

Electrical
Specific volume resistance
Loss angle tangent frequency
Relative dielectric permeability
Chemical Resistance
% weight loss after 3 hrs boiling in:
H2O
2n NaOH (Sodium Hydroxide)
2n HCI (Hydrochloric acid)

(%)
(%)
(%)

Price Comparison

Mold (Tool) Making

Asphalt
Ballistics
Bridge Wraps
Manholes

What Application do you have

that needs Better Performance
at a Better Price?

Basalt Sample Packs

Order Online
A wide assortment of our products are available in Sample

Basalt Woven Fabric can be

supplied with the following
coating on one or both sides

Packages to allow you a chance to physically feel and see

COATING TYPE

PURPOSE

them before deciding on future purchases. Order online at

Thermoblocker

Intumescent barrier

www.smarter-building-systems.com/basalt-sample-packs/.

Flock

Skin contact barrier

We can also put together Custom Sample Packs.

Silicon

Splatter protection

Phone (401) 481 8422 or email Nick today

Acrylic

Splatter protection

for more Information and Technical Data.

PUR or EVA

Fatigue resistance